HLC-1000J CPVC Pipe Extrusion Resin
Tel : 0086-18753636550
Email : service@rikechem.com
Contact Us

Product Details

Description

Rike CPVC extrusion resin HLC-1000J is a chlorinated polyvinyl chloride resin developed using Rike’s unique technology. CPVC is characterized by heat resistance which has been improved by 20 to 40°C without harming PVC's physical and chemical properties. CPVC can be used in applications under high temperatures, where general purpose PVC would soften, rendering it useless. HLC-1000J is applied to CPVC sprinkle, industrial and hot water CPVC pipes.

Benefits

* High Vicat Softening Temperature

* High Flame Resistance and Low-smoke Generation

* Excellent impact strength

* Chemical and Corrosion Resistance

Specification

Specification

Unit

Test standard

HLC-1000Z

Appearance

White powder

Bulk density

g/cm3

GB/T 1636-2008

0.50-0.52

Sieve residue, 30 mesh

%

GB/T 2916

≤1.0

Volatile content

%

ASTM D5668

≤0.40

Specific gravity

g/cm³

GB1033-70

1.45-1.55

Mechanical properties


Test condition

Test standard

HLC-1000Z formula

Control

Charpy impact strengthRoom temp.KJ/m2

24±1℃

GB/T 1043

25.20±1.79

23.54±1.87

Charpy impact strengthLow temp.KJ/m2

0±1℃

GB/T 1040

18.08±1.05

17.01±0.28

Vicat softening point ℃

120℃/h

GB/T 8802

115.1

114.2

Test formula: CPVC resin 100phr, stabilizer 2.6phr, lubricant 3phr, impact modifier 8.0phr

Application

HLC-1000J is applied to CPVC sprinkle, industrial and hot water CPVC pipes.

图片2.jpg


Packaging and storage

25Kg/bag or 500-650kg big bags. The product should be kept clean during transportation and loading and unloading to prevent sun, rain, high temperature and humidity, and avoid damage to the packaging. It should be stored in a cool, dry, no direct sunlight, temperature lower than 40 ℃ warehouse, the storage period is two years. After two years, it can still be used after performance test is approved.